Preservation Methods of Eggs in Freezer

1. Coating Preservation Method

Liquid paraffin is often used as coating agent due to its low toxicity and small rancidity corrosive effect. In addition, solid paraffin, vegetable oil, alginic acid amines, polystyrene, polyvinyl alcohol, styrene butadiene, acrylic resin, polyvinyl chloride resin, gliadin and poly maltotriose can also be used as coating agents. No matter what kind of coating agent is used, it should be harmless to human body and with no side effects.

There are two kinds of coating methods: dipping and spraying. Spraying method is more commonly used. Eligible eggs after examination can be dipped or sprayed. After getting dry naturally, eggs can be packed for storage.If combined with cryopreservation methods, the preservation effect is better. 

2. Pasteurization Preservation Method

     Pasteurization process: first, put the eggs into the special wire basket, 100 to 200 per basket will be the most appropriate. Then sink the egg baskets into hot water of about 95-100℃. Take them out immediately after soaking 5 to 7 seconds. When the shell becomes dry and the egg temperature is lowed, the eggs can be stored.

    

3. Cave Cold Storage Method

Whether there is cave freezer, this method can be applied to store eggs. Outside the cave freezer is equipped with a cooling fan which can deliver cold air inside the cave. Load qualified eggs into wooden crates or cardboard boxes, stacking into a stack. Let cold air pass through each stack. Keep the temperature at 4 ~ 5 ℃, humidity of 75% to 80%. The eggs can be fresh for 4 to 6 months.

3. Peracetic Acid Preservation Method

Dilute peracetic acid into aqueous solutio with a concentration of 1-2g/l. Soak eligible eggs into the solution for three to five minutes. Take them out and dry them for storage. If store them into freezer, the preservation time could be longer.

What’s the Difference Between PVA 1788 and PVA 1799?

The type of PVA frequently used in construction paint is PVA 1788 and PVA 1799.

Polyvinyl alcohol is obtained by the hydrolysis of polyvinyl acetate, it can not be obtained directly from the polymerization of vinyl alcohol, because vinyl alcohol is very unstable. Free vinyl alcohol monomer can not be existed. 

The molecular formula weight of PVA is (C2H4O)x. Its physical properties can be greatly affected by the degree of hydrolysis and polymerization degree. Its degree of polymerization of polyvinyl alcohol can be divided into high degree, medium degree and low degree of polymerization. Recently a new kind of products with ultra-high degree of polymerization is developed. There are usually three kinds of hydrolysis degrees, that is 78%, 88% and 98%. 98%-100% is complete alcoholysis PVA, 87%-89% is part alcoholysis PVA. PVA1788 usually means the polymerization degree is 1700 while the hydrolysis degree is 88%. PVA 1799 means the polymerization degree is 1800 while the hydrolysis degree is 99%      

Polyvinyl alcohol solution of complete alcohol solution is 98 % to 100% , alcoholysis alcoholysis is usually part of 87% to 89% , in order to facilitate said polymerization degree often take hundreds and thousands digits on the front, the percentage of alcohol solution of the behind , thus PVA-1788 means that the degree of polymerization of 1700 , degree of hydrolysis of 88%, PVA-1799 indicates a degree of polymerization of 1700 , degree of hydrolysis of 99 %. PVA 1788 is partly alcoholyzed product while PVA1799 is completely alcoholyzed product.

Then what is partly alcoholysis and what is complete alcoholysis? Complete alcoholysis means this kind of PVA will not be soluble unless the heat is up to 95 degree. While for partly alcoholyzed PVA, it can be soluble when the temperature is 85 degree.

Polyvinyl Alcohol Environmental Protection Adhesive

Polyvinyl alcohol environmental protection adhesive is a new non-polluting, fast-drying water-based adhesive. It is used for the production of man made panels. 

Compared with the same adhesive on the market at present, it does not contain formaldehyde and other toxic ingredients. It will not influence the production and using environment. The cost is low, the process is simple, the bonding effect is good and the speed of solidification is fast. 

The formula of Poly(vinyl alcohol) environmental protection adhesive 

Formula One

Raw materials:

polyvinyl alcohol 0-8%, polyvinyl acetate or ethylene - vinyl acetate or mixture latex (N'XN 50Z) 1-40%. Appropriate modifier and thickening agent; water: 55% to 88%; cement or plaster and its retarder or activator: 3 % to 25%.

　　

Preparation Methods: add 30g of polyvinyl alcohol to a heating pot containing 400g of water, stir and heat to 90 ~ 100℃. Keep stirring for about half an hour until polyvinyl alcohol is completely dissolved, then cool to below 80℃. Add 300g of polyvinyl acetate ethylene (content 50%), thickeners 20g, then add water to make the total quantity 900g. The above belongs to A group. Add B group when in use: 100g of white cement containing tricalcium silicate and dicalcium silicate or 100g of hemihydrate gypsum or its retarder, stir evenly, then sizing, realize pollution-free cold wood-based panel production .

　

Formula Two

Ingredients: PVA: 5% to 11%, appropriate amount of modifier, 65% to 88% of water; cement or plaster and its retarder or activator: 5 % to 25%

Preparation Methods: add 75g of polyvinyl alcohol to a heated pot containing 750g of water, stir and heat to 90 ~ 100℃, stir for half an hour at the same temperature until it is completely dissolved, then add proper amount of modifier Jun amount and then water to make a total of 880g. That is A group. B group will be 120g of white cement and activator or 100g of hemihydrate gypsum and its retarder, stir, then sizing, then produce pollution-free cold wood-based panel.　

Most Eye Drops Containing Preservatives

Many office workers and students have to stare at computers for a long time everyday for work and study. When they feel their eyes dry, they would use eye drops to wet their eyes. To many of us, eye drops have become a necessity of our daily life.

Several reporters visited some drugstores recently and found that there are about a hundred kinds of eye drops together including taurine eye drops, new rohto eye drops, retro neomycin sulfate eye drops, polyvinyl alcohol eye drops, houttuynia eye drops and man other different types.

“Give me a bottle of eye drops which had better have no preservatives.” At a drugstore, a staff recommended a type of eye drop called polyvinyl alcohol eye drops after inquiring the symptoms the reporter has, because among the hundreds of eye drops, only this type indicates on its label that it contains no preservatives. 

Does each type of eye drops contain preservatives? When reporters asked this question to drugstore staff, they found that most of them are not clear with this question. “Even if they are with preservatives, the quantity is very small and has no harm on eyes.” Most of the staff answered like this.

In fact, apart from the eye drops used by adult contains preservatives, eye drops used by children also do. While those people who come to the drugstore to buy eye drops only choose eye drops according to their symptoms instead of caring whether they contain preservatives or not.

Reporters notice that although most eye drops contain preservatives, there is no indication of it on the package or the instructions. Some other products only indicate benzalkonium chloride in its ingredients. People with no chemical knowledge will not know that is the preservative.

Therefore, if you decide to buy eye drops for yourself or your children, you should first check whether they contain preservatives or not. You should take priority to those indicating that preservatives are not contained such as PVA eye drops or carefully inquire doctors before you go and buy a type of eye drops all by yourself.      

Introduction of World Special PVC resins

PVC resin is one of the five general used resins in synthetic material. It is with good physical and mechanic properties. Its production capacity comes the second place, rank only second to polyethylene. PVC resin can be used to produce construction materials, packaging materials, electronic materials and daily used products. It has wide application in industrial, agricultural, construction, transportation and many other fields. Currently, the consumption of PVC is mainly hard products, about 59.83% of the total consumption. Soft products are about 32.88% and others 7.29%. PVC resin usually contains two types: general type and special type. The general one is about 90% of the total and the special one only takes up 10%.

There is no specific definition on special PVC resin. One popular saying abroad is that all resins that can provide special usage in comparison with normal resins can be called special PVC resin. The generally used special resins abroad mainly include: blending resin, special emulsion resin, powder processing resin, special suspension resin, ultra high molecular weight resin, super absorption resin, matting resin, copolymer resin, polyethylene and vinyl acetate copolymer resin, solution polymerization resin and so on.

Among those specially used PVC resin, polyethylene and vinyl acetate copolymer resin is one very popular in recent years. It includes Vinyl Copolymer Resin, Vinyl Terpolymer Resin With Carboxyl Function Group (the so called UMCH) and Vinyl Terpolymer Resin With Hydroxyl Function Group (the so called UMOH). They are widely used for the production of ink, paint and Gold And Silver Cardboard.